High temperature alloy chloridation at 850°C
2007
The resistance of eight alloys against chloridation was tested at 850 °C in Ar/Cl 2 (2.5% Cl 2 ) for 15 min. Pre-oxidation treatments were performed for 1 h and 8 h at 850°C in order to produce a thin, adherent and protective oxide scale able to improve the chloridation behaviour of the tested materials. The chloridised sample morphologies were compared to the morphologies observed on the non pre-oxidised samples. The alloys containing a large amount of iron did not exhibit any chloridation resistance, even after pre-oxidation, and were severely damaged. The nickel based alloys gave interesting results but were also attacked by chloride, probably by the "active oxidation" mechanism. The dur…
Anwendung der Mößbauer-Spektroskopie auf die Untersuchung von Deckschichten in Naturumlaufkesseln
1978
57Fe-Mosbauer-spektroskopische Transmissions- und Reflexionsmessungen wurden zur Aufklarung der qualitativen und quantitativen Zusammensetzung von Deckschichten auf der Innenseite von Rohren aus Naturumlaufkesseln vorgenommen. Die Deckschichten waren bei 120 bis 174 atu, 320 bis 353 °C, einem pH-Wert zwischen 9,5 und 10,5 und einem Gehalt an P2O5 und SiO2 von < 10 bzw. < 4 mg/l auf den Rohrinnenflachen (Werkstoff 15 Mo 3: 0,12%C, 0,15% Si, 0,5% Mn, 0,04% P, 0,04% S, ⩽ 0,3% Cr, 0,25% Mo, Rest Fe; St. 45. 8. III: < 0,22% C, 0,1% Si, ⩾ 0,45% Mn, 0,05% P, 0,05% S, ⩽ 0,3% Cr, Rest Fe) innerhalb von maximal 127000 h entstanden. Die Mosbauer-spektroskopischen Untersuchungen, unterstutzt durch eine…
Statistical prediction of corrosion front penetration
1997
A statistical method to predict the stochastic evolution of corrosion fronts has been developed. The method is based on recording material loss and maximum front depth. In this paper we introduce the method and test its applicability. In the absence of experimental data we use simulation data from a three-dimensional corrosion model for this test. The corrosion model simulates localized breakdown of a protective oxide layer, hydrolysis of corrosion product and repassivation of the exposed surface. In the long time limit of the model, pits tend to coalesce. For different model parameters the model reproduces corrosion patterns observed in experiment. The statistical prediction method is base…